Passage of water at recommended flow rates through the resin as supplied can achieve almost complete reduction of total dissolved solids. The residuals produce average conductivity values of about 0.1 µs cm-1 for a major portion of the service run which may be extended depending upon the final water quality acceptable. Equivalent volumes of ultra pure water may be obtained after regeneration but only if sufficient regenerant quantities are employed to achieve the percentage conversion levels equivalent to those of the "as supplied" resin. Generally acceptable capacity and quality is obtained economically at lower regeneration.

• Typical physical & Chemical characteristics

    Guaranteed Sales Specification               OH ^- Form                   H ⁺ Form         

         Polymer Matrix Structure              Gel PolyStyrene Crosslinked with DVB       

                                                                  Anion                         Cation            

                Functional Group                 Quaternary Amine            Sulfonic acid       

                   Volume ratio                              50%                            50%            

      Total Exchange Capacity, min.               1.3meq/l                      1.9meq/l         

          Water Retention Capacity                 53%-60%                    45%-50%        

                >1.25 mm max.                            5%                              5%              

                <0.40 mm, max.                           2%                              2%              

           Whole Bead Count, min.                     95%                            95%             

   Moisture Content as shipped, max                                 65%                              

               PH Range, Stability                                          0-14                               

         Shipping weight (approx.)                                 705-740 g/l                          

            Ionic conversion, min.                       90%                            99%