MAGCRAFT - Model NSN0570 -Cube Magnets
These cube magnets are 0.125"(3.2mm) Long x 0.125"(3.2mm) Wide x 0.125"(3.2mm) Thick. They are magnetized through the thickness. They are composed of grade 40 neodymium iron boron magnetic material and are plated in nickel-copper-nickel for a shiny corrosion resistant finish. Their individual pull force is approximately 1.5 lbs. Maximum working temperature is 176 F (80 C).
These cube magnets are 0.125"(3.2mm) Long x 0.125"(3.2mm) Wide x 0.125"(3.2mm) Thick. They are magnetized through the thickness. They are composed of grade 40 neodymium iron boron magnetic material and are plated in nickel-copper-nickel for a shiny corrosion resistant finish. Their individual pull force is approximately 1.5 lbs. Maximum working temperature is 176 F (80 C).
- Part Number : NSN0570
- Imperial Dimensions : 0.125 inch long x 0.125 inch wide x 0.125 inch thick
- Metric Dimensions : 3.175mm long x 3.175mm wide x 3.175mm thick
- Material : Sintered Neodymium-Iron-Boron (NdFeB)
- Shape : Cube
- Plating : Ni-Cu-Ni (Nickel)
- Magnetization Direction : Thickness
- Grade : N40
- Pull Force (lbs[g]) : 1.51[685]
- Surface Field(G) : 4123
- Maximum Operating Temperature : 80 Deg C (176 Deg F)
- Dimensional Tolerance : +/-0.005"
- Magnet Quantity : 100
- Volume (cm3) : 0.03
- Weight (g) : 0.24
- Brand : Magcraft
- Packaging : Magpak Tube
- UPC : 897970000709
- Remanent Flux Density Br (kG [T]) : 12.5-12.8 [1.25-1.28]
- Coercivity HcB (kOe [kA/m]) : >=11.3 [>=923]
- Intrinsic Coercivity HcJ (kOe [kA/m]) : >=12.0 [>=995]
- Maximum Energy Product Bhmax (MGOe [kJ/m3]) : 38-41 [302-326]
- Density p(g/cm3) : >=7.45
- Compression Strength (Mpa) : 600-1200
- Bending Strength (Mpa) : 150-380
- Vickers Hardness (HV) : 460-660
- Recoil Permeability (urec) : 1.05
- Electrical Resistance (Ohm*mm2/m) : 1.25-1.55
- Curie Temperature Tc (�C) : 310
- Thermal Expansion Coefficient 100�C//(x10^-6/K) : 6
- Thermal Expansion Coefficient 100�C?(x10^-6/K) : -1