• Asiamet is a manufactures and suppliers in India. We bring forth an impregnable range of wear resistant steel plate. These high grade wear resistant steels are extensively used across different industrial sectors for various purposes. We take into account the variegated needs of our international clients and offer suitable range of wear resistant steels Following are the technical specifications of this wear resistant steel.
• Abrasion resistant steel is used in areas where there is likely to be a high degree of abrasion or wear of the steel plate. Typical applications are in truck beds, attachments to diggers and earth movers and in processing applications in the mining industry.
• The key quality for wear resistant steels is their hardness We sell wear plate according to its hardness measured on the brunel hardness test- usually in 400HB grades. 400 HB steel is over 3 times harder than mild steel (120HB), but only a third as hard as stainless steel (1S0HB). Example uses are for construction machinery, skips bulldozers and excavators, buckets and conveyors.
• The steel is quenched which provides wear resistance: in order to improve hardness it may also be tempered. Lower HBs generally provide good cold bending properties and good weld ability is not generally reduced as the hardness increases Wear resistant steels are not appropriate for use at temperatures over 2S0 degree C as the heat can cause changes to the material properties.

Product: Wear Resistant Plates

Thickness (mm): 3mm - 200mm

Width (mm): 500 - 3000mm

Grade: 200, 400, 450, 500

Finish: Hot rolled plate (HR). Cold rolled sheet (CR)

Price Terms: Ex-Works, FOB, CIF. CFR, CNF

Latest Price: Call +919619672006

Email: sales@asiametsteel.com

• Truck dump bodies
• Scrap presses and paving molds.
• Mining and earth-moving machinery
• Conveying crushing and pulverizing equipment
• The steel may be used at the discretion of the purchaser for wear-exposed structures, excavating
• The processing and application techniques as a whole are of fundamental importance for the successful use of the products fabricated of this steel