KCM Special Steel - Model incoloy 800h -nickel alloy incoloy 800h pipe

The Cr content in the Nickel Alloy Incoloy 800H Pipes And Fittings  is typically 15-25%, the nickel content is 30-45% and contains a small amount of aluminum and titanium.
800H alloy from the high temperature after the cold are in the austenite single zone, therefore, the use of a single austenite structure.
The alloy has a high chromium content and a sufficient nickel content, so it has a higher resistance to high temperature corrosion and is more used in industry.
In the chloride, low concentration of NaOH aqueous solution and high temperature and high pressure water, has excellent resistance to stress corrosion cracking performance, so for the manufacture of stress corrosion cracking equipment.

Nickel Alloy Incoloy 800H Pipes And Fittings domestic and foreign counterparts Grade:

 
CN
GB
USA
UNS
Germany
SEW VDIUV
UK
BS
Incoloy 800H
NS1102
N08810
W.Nr.1.4958
X5 NiCrAlTi 31-20
NA15(H)
 

Nickel Alloy Incoloy 800H Pipes And Fittings  Supply Specifications:
Round bar, bar, strip, pipe, seat, spheres, flanges and forgings

Nickel Alloy Incoloy 800H Pipes And Fittings Chemical composition:
Alloy
C
Mn
Si
P
S
Cr
Ni
Cu
Ti
Al
Fe
Incoloy 800H
0.05
～0.10
≤1.50
≤1.00
≤0.030
≤0.015
19.0
～23.0
30.0
～35.0
≤0.75
0.15
～0.60
0.15
～0.60
38.0
～47.0
 

Nickel Alloy Incoloy 800H Pipes And Fittings Physical properties:

Density
8.0g/cm3
Melting point
1350-1400℃
Nickel Alloy Incoloy 800H Pipes And Fittings The minimum mechanical properties of alloys at room temperature:

Alloy
T S
Rm N/mm2
Y S
RP0.2N/mm2
Elongation
A5 %
800H
450
180
35
Nickel Alloy Incoloy 800H Pipes And Fittingshas the following features:
1. Excellent corrosion resistance in extremely high temperature aqueous media up to 500 ° C
2. Good resistance to stress corrosion
3. Very good workability

Nickel Alloy Incoloy 800H Pipes And Fittings metallographic structure:
Nickel Alloy Incoloy 800H Pipes And Fittings is a face-centered cubic lattice structure. The extremely low carbon content and the increased Ti: C ratio increase the stability of the structure and the greatest resistance to abrasion as well as the resistance to intergranular corrosion. A low temperature annealing around about 950 ° C ensures a fine grain structure.

Nickel Alloy Incoloy 800H Pipes And FittingsCorrosion resistance:
Nickel Alloy Incoloy 800H Pipes And Fittings can withstand many corrosive media corrosion. Its high nickel content in the water-based corrosion conditions have a good resistance to stress corrosion cracking performance. High chromium content to have a better resistance to corrosion and crevice corrosion cracking performance. The alloy has a good resistance to nitric acid, organic acid corrosive, but in sulfuric acid and hydrochloric acid in the corrosion resistance is limited. In addition to the possible corrosion of the halide, there is a good corrosion resistance in oxidizing and non-oxidizing salts. In water, steam and steam, air, carbon dioxide mixture also has a good corrosion resistance.

Nickel Alloy Incoloy 800H Pipes And FittingsProcess performance and requirements:
Thermal processing
1, the temperature range of 1200 ℃ ~ 950 ℃, cooling water quenching or rapid air-cooled.
2, in order to get the best performance and creep resistance, after hot processing to be solution treatment.
3, the material can be directly into the furnace has been heated to 1200 ℃, warm enough time after the rapid baked, in the specified temperature range for thermal processing. When the material temperature falls below the hot working temperature, need to reheat.
Cold working
1, the work hardening rate is greater than the austenitic stainless steel, so the need for processing equipment selection. The cold working material should be a solution heat treatment and should be intermediate annealed when the amount of cold working is large.
2, if the cold processing capacity is greater than 10%, you need to work on the secondary solution solution.