Blue Gard Style 3200 Gasketing Brochure

MATERIAL PROPERTIES*Color: Off-whiteComposition: Aramid fibers with a SBR binderFluid Services1: Water, saturated steam4, inert gasesTemperature2, °F (°C)Minimum: -100 (-73)Continuous Max: +400 (+205)Maximum: +700 (+371)Pressure2, Maximum, psig (bar): 1200 (83)P x T (max.)2, psig x °F (bar x °C)1/32 and 1/16": 350,000 (12,000)1/8": 250,000 (8,600)Meets Specification: ABS (American Bureau of Shipping) and MIL-DTL-24696C6TYPICAL PHYSICAL PROPERTIES*ASTM F36 Compressibility, range, %:ASTM F36 Recovery, %:ASTM F38 Creep Relaxation, %:ASTM F152 Tensile, Across Grain, psi (N/mm2): ASTM F1315 Density, lbs./ft.3 (grams/cm3):ASTM F433 Thermal Conductivity (K), W/m°K (Btu.·in./hr.·ft.2·°F):ASTM D149 Dielectric Properties, range, volts/mil.Sample conditioning 1/16" 1/8"3 hours at 250°F: 508 285(3)96 hours at 100% Relative Humidity: 116 140ASTM F586 Design Factors 1/16" & Under 1/8""m" factor: 3.5 6.6"y" factor, psi (N/mm2): 2100 (14.5) 3000 (20.7)ASTM F104 Line Call Out:SEALING CHARACTERISTICS*Gasket Load, psi (N/mm2):Internal Pressure, psig (bar):LeakageIMMERSION PROPERTIES*- ASTM F146 Fluid Resistance after Five HoursNotes:6 To ensure receipt of product branded Mil-G-24696, certification will be required- - fees associated based on quantity. Refer to "Military Specifications" in the Gasketing Terms section of the Engineered Gasket Products catalog for order/inquiry requirements.580 (40)3 Indicates current arced around and not through gasket. Dielectric higher than indicated.4 These styles are not preferred choices for steam service, but are successful when adequately compressed. Minimum recommended assembly stress = 4,800psi. Preferred assembly stress = 6,000-10,000psi. Gasket thickness of 1/16" strongly preferred. Retorque the bolts/studs prior to pressurizing the assembly. For saturated steam above 150psig or superheated steam, consult Garlock Engineering.5 Fourth numeral 9: % Thickness Increase in IRM Oil #903 = 25-50% max. A9: Leakage in Fuel A (Isooctane), Gasket Load = 500psi (3.5N/mm2), Pressure = 9.8psig (0.7bar): Typical = 0.1ml/hr, Max = 1.0ml/hr. A9: Leakage in Nitrogen, Gasket Load = 3,000psi (20.7N/mm2), Pressure = 30psig (2bar): Typical = 0.4ml/hr, Max = 1.0ml/hr. M9: Tensile Strength = 2,250psi min. (15N/mm2 min.).0.4 ml/hr. 0.03 cc/minThis is a general guide and should not be the sole means of selecting or rejecting this material. ASTM test results in accordance with ASTM F-104; properties based on 1/32" (0.8mm) sheet thickness unless otherwise mentioned.* Values do not constitute specification Limits-Tensile Loss, (%)2 Based on ANSI RF flanges at our preferred torque. When approaching maximum pressure, continuous operating temperature, minimum temperature or 50% of maximum PxT, consult Garlock Applications Engineering. Minimum temperature rating is conservative.ASTM F37B ASTM F37B DIN 3535- 4Fuel A Nitrogen Gas Permeability4640 (32)9.8 (0.7)<2570-85°F (20-30°C)5-20<70 -- <301 See Garlock chemical resistance guide.-0-1515-30ASTM Fuel A70-85°F (20-30°C)300°F (150°C)ASTM Fuel BWeight Increase, (%) <20Thickness Increase, (%) 0-107-1750182250 (15)300°F (150°C)ASTM IRM #9030.1 ml/hr.30 (2)Garlock BLUE-GARD® 3200F712902A9B4E45K5L102M9(5)0.29-0.38 (2.00-2.65)100 (1.60)ASTM #1 Oil500 (3.5) 3000 (20.7)